Progress in Plasma Processing of Materials, 2003

ISBN Imprimer:
ISBN En ligne:


A. A. Syed
SPCTS, Universite de Limoges, Faculte des Sciences, Limoges, France

P. Denoirjean
SPCTS, Universite de Limoges, Faculte des Sciences,123 ave. A. Thomas, 87060, Limoges, France

Alain Denoirjean
Equipe Plasma Laser Matériaux, ESA CNRS 6015, 87060 Limoges Cedex, France

J. C. Labbe
Faculte des Sciences et Techniques, L.M.C.T.S. - C.N.R.S. E.S.A. 6015 Universite de Limoges -123, av. Albert Thomas - 87065 LIMOGES Cedex, France

Pierre Fauchais
Laboratoire Sciences des Procedes Ceramiques et de Traitements de Surface UMR CNRS 6638 University of Limoges 123 avenue Albert Thomas, 87060 LIMOGES - France


When spraying on a smooth surface (Ra < 0,05 µm), two types of splats can be observed: disk shaped ones and extensively fingered ones - the transition between both depending on a substrate critical temperature (Tc). Even when Ts > Tc the splat shape depends strongly on the substrate surface oxidation stage; the aim of this paper being to study this effect. For that two substrates have been chosen: low carbon 1040 steel and low alloy steel with 1.6 wt % Cr. Alumina and 316L austenitic stainless steel particles have been sprayed with a d.c. plasma torch (PTF4 type) with a 7 mm internal diameter anode nozzle. For these substrates and particles, the transition temperature was found to be Tc ~300°C. Extensively fingered splats were obtained after preheating substrates to temperatures higher than 380°C. These substrates have been, thus, plasma preheated at 400°C and 450°C in air or nitrogen atmosphere.
Splats with bubbles were created on oxidized 1040 substrates with a morphology that suggests an expulsion of entrapped gases from the underneath porous oxide layer. The entrapped gases could also explain the splashing of splats on substrates preheated to temperatures higher than Tc. A higher degree of splashing was observed in 316L steel splats compared to A12O3 ones keeping the same substrate conditions. Average splat diameter (D) decreases with an increase in formed oxide layer thickness. At Ts = Tc, flattening degree for steel splats were of order 1.2 higher than those of Al2O3. Splashing can be suppressed by preheating the substrates with an oxygen free gas flowing around the substrates that results in limiting the oxidation and substrates can be maintained at higher temperatures.