PULSED PLASMA DEPOSITION OF OXIDE HARD COATINGS

要約

In the last years a variety of plasma sources have been developed for film deposition by magnetron sputtering. In addition to RF- and DC-sputter sources, pulsed plasma sources are gaining increased attention in sputter technology. This interest is driven by the wish of depositing coatings with superior properties as compared to those deposited by conventional techniques. One prominent example of coatings that are significantly enhanced by the usage of pulsed sputter deposition is alumina. Although crystalline α-aiumina can be deposited by thermal CVD at temperatures above 1000 °C for two decades, no process for the deposition of crystalline alumina at low temperatures is commercially available up to now.
In this paper, the results of a detailed study of the plasma parameters during bipolar pulsed magnetron sputtering and their effect on the properties of alumina hard coatings Is reported. Langmuir type voltage measurements at the substrate position, optical emission spectroscopy as well as mass spectroscopy were used to monitor the effect of target poisoning on the reactive deposition of alumina. Those principal observations were connected to easily available process parameters like discharge voltage and oxygen partial pressure. Based on these measurements, the deposition of crystalline γ-alumina with high hardness and good adhesion under technical conditions was achieved.
ホーム Begell Digital Portal Begellデジタルライブラリー ジャーナル 書籍 電子書籍 参考文献と会報 著者、編集者、レビュー者 A-Z商品インデックス 価格及び購読のポリシー Begell Houseの概要 連絡先 Language English 中文 Русский 日本語 Português Deutsch Français Español